| Description |
Results |
Test Method |
| Dropping Point (126.7° C min.) |
>600° F |
ASTM D-2265 |
| Unworked Penetration |
260 |
ASTM D-1403 |
| Worked Penetration |
220 |
ASTM D-1403 |
| NLGI Number |
3 |
NLGI |
| Consistency |
Soft |
Visual |
| Color |
Cream |
Visual |
| Resistance to Aqueous Solutions - Distilled Water |
Pass; no deterioration |
FTM-5415 |
| Resistance to Aqueous Solutions - Ethanol: Water 50:50 Mix |
Pass; no deterioration |
FTM-5415 |
| Resistance to Fuel/Appearance |
Pass |
FTM-5414 |
| Fuel Solubility (20% max.) |
1.11% |
FTM-5414 |
| Water Spray Off |
2.33% |
ASTM D-4049 |
| Water Washout at 175° F (Bearing Dried at 77° C) |
6.63% |
ASTM D-1264 |
| Load Wear Index |
74.09 |
ASTM D-2596 |
| Load Wear Index (Last Non-Seizure [scar]) |
160kg (0.48 mm) |
ASTM D-2596 |
| Load Wear Index (Last Seizure [scar]) |
200 kg (0.71 mm) |
ASTM D-2596 |
| Load Wear Index (Weld Load) |
250 kg |
ASTM D-2596 |
| Copper Corrosion (#1b max.) |
Shiny 1b |
FTM-5309 |
| Film Stability and Corrosion on Steel |
Pass; no corrosion |
¶4.6.3 |
| Roll Stability - Original Penetration |
271 |
ASTM D-1831 |
| Roll Stability - After Rolling Penetration |
275 |
ASTM D-1831 |
| Roll Stability - Change in Penetration |
+4 |
ASTM D-1831 |
| Roll Stability - Percent Change |
+1.48% |
ASTM D-1831 |
| EMCOR Rust Test, Bearing A |
#4 |
ASTM D-6138 |
| EMCOR Rust Test, Bearing B |
#5 |
ASTM D-6138 |
| Dielectric Strength |
112 volts/mil |
ASTM D-149 |
| Breakdown Voltage |
5,597 volts |
ASTM D-149 |
| Dissipation Factor @ 1 kHz/73°F/50%R.H. |
0.0782 |
ASTM D-150 |
| Dielectric Constant |
5.95 |
ASTM D-150 |
| Low Temperature Torque at 0° F - Starting Torque |
55,250 g-cm |
ASTM D-1478 |
| Low Temperature Torque at 0° F - 1 Hour Running Torque |
2,990 g-cm |
ASTM D-1478 |