AC Tech 615B-2 Low Adhesion Access Door Sealant (Chromated) - AMS3267B2

Two Part Sealant: 1. Holding the cartridge, grasp the dasher rod and pull back approximately one inch.

2. Insert the ramrod into the hollow of the dasher rod, break the piston loose, and inject about 1/3 of the contents into the cartridge.

Note: Do not inject all of the catalyst in one location. Distribute evenly throughout base material.

3. Repeat steps 2 and 3 until all the contents of the rod are emptied into the cartridge. Remove the ramrod.

4. Mix for the required number of strokes (hand mixing) or for the required amount of time (machine mixing) indicated in the kit intructions.

5. When mixing is complete, remove bottom cap.

6. Pull the dasher rod back to the neck of the cartridge, grasp the cartridge firmly at the neck, unscrew the dasher rod and remove.

7. Screw the nozzle into the cartridge, insert into the extrusion gun and use as required. For hand extrusion, press the used dasher rod against the plunger to force the material from the cartridge.

Storage

The shelf life of AC-615 Class B is 12 months from date of packaging, when stored at temperatures below 80 degrees F in its original container.

Mixed AC-615 Class B may be stored under refrigeration as follows: 15 days at -10 degrees F, 30 days at -40 degrees F. It is important to remember that freezing, storing and thawing procedures reduce application life. Also, frozen storage will reduce application life by varying amounts depending on the storage temperature and length of storage time. All aspects of storage, freezing and thawing should be planned carefully and it is not recommended to mix and freeze with less than 1/2 hour application time.

Health and Safety Precautions

AC-615 Class B sealant is safe to use and apply when recommended precautions are followed. Before using this product, read and understand the Material Safety Data Sheet (MSDS), which provides information on health, physical and environmental hazards, handling precautions and first aid recommendations. An MSDS is available upon request. Avoid overexposure. Obtain medical care in case of extreme overexposure.

Typical Physical and Application Properties

Application Life and Cure Time
(At 75 degrees F, 50% Relative Humidity)

B-1/2

B-2

*Application life refers to the length of time that mixed compound remains at a consistency suitable for application with spatula or caulking gun. Application life is always measured at a standard temperature of 77 degrees F with a relative humidity of 50%. In general, for every 20 degree rise in temperature, the application life is halved; and for every 20 degree drop, it is doubled. High humidity levels during the mixing process will shorten application life.

**Tack-free time is the length of time after which a mixed sealant will no longer tightly adhere to LP-P-690 standard low-density polyethylene film.

***Cure time is defined as the length of time it takes AC-615 Class B sealant to reach 30A hardness. It depends on three factors: remaining application life, temperature and relative humidity. The temperature/humidity factors for application life also apply to curing. To accelerate the curing process, apply heat up to (but no more than) 120 degrees F.

Typical Physical and Performance Properties of Cured Compound